Título: | Estudo de defeitos na indústria têxtil |
Outro(s) título(s): | Study of defects in the textile industry |
Autor(es): | Gonçalves, Ana Sofia da Silva |
Orientador(es): | Souto, A. Pedro Rocha, A. M. |
Palavras-chave: | Defeito Indústria têxtil Controlo de qualidade Estamparia Acessórios metálicos Defect Textile industry Quality control Stamping Metal accessorries |
Data: | 9-Mar-2022 |
Resumo(s): | Um dos grandes problemas da indústria têxtil, passa pela existência de uma elevada
quantidade de defeitos que podem surgir ao longo das produções. Por isso mesmo, é
importante realizar estudos pormenorizados de defeitos e para se descobrir a causa, ajudando
as empresas a direcionarem as suas produções para uma minimização de defeitos através de
conhecimento e da forma que devem proceder quando estes aparecem ou,
preferencialmente, precaverem a ocorrência de defeitos.
Nesta dissertação apresenta-se o estudo de caso de três defeitos (A, B e C), com origens e
causas distintas, que ocorreram na indústria têxtil. Os defeitos estudados foram problemas
litigiosos entre empresas do setor têxtil, razão pela qual neste trabalho, não vai ser
mencionado o nome. A abordagem adotada inclui, a análise do defeito presente na peça
rececionada e, sempre que possível, a reprodução do defeito laboratorialmente.
No estudo de caso do defeito A, analisou-se um estampado por sublimação que se
apresentava pouco uniforme e com cores esbatidas.
No estudo de caso do defeito B, examinou-se o aparecimento de uma mancha, na zona de
aplicação de elementos metálicos designados de “Buckles”, em macacões infantis tingidos.
No estudo de caso do defeito C, estudou-se um estampado direto aplicado em dois tipos de
malhas (t-shirts e sweats) que apresentava quebras em várias cores.
Com esta dissertação pretende-se aprofundar o conhecimento sobre as causas de alguns
defeitos e mostrar de que forma devem ser analisados e prevenidos por parte das empresas
deste setor. Sendo este um problema que é muito comum nesta indústria é importante que
se conheçam as causas dos mesmos para que não voltem a acontecer em futuras produções. One of the major problems of the textile industry is the existence of a high amount of defects that can occur during the production. For this reason, it is important to carry out detailed studies of defects to discover the cause, helping companies to direct their production towards a minimization of defects through knowledge of the way to proceed when they occur or, preferably, prevent the occurrence of defects. This dissertation presents the case study of three defects (A, B and C), with different origins and causes, which occurred in the textile industry. The defects studied are based on litigious problems between companies in the textile sector, which is why the names of the companies involved will not be mentioned in this work. The approach adopted includes analyzing the defect present in the sample received and, whenever possible, reproducing the defect in the laboratory. In the case study of defect A, we analyzed a print by sublimation that was not very uniform and had faded colors. In the case study of defect B, the appearance of a stain in the area of application of metallic elements called “Buckles” in dyed children's overalls was examined. In the case study of defect C, a direct print applied to two types of knits (t-shirts and sweats) that showed breaks in several colors was studied. This dissertation intends to deepen the knowledge about the causes of some defects and show how they should be analyzed and prevented by companies in this sector. Since this is a problem that is very common in this industry, it is important that the causes are well known so that they can be prevented in future productions. |
Tipo: | Dissertação de mestrado |
Descrição: | Dissertação de mestrado integrado em Engenharia Têxtil |
URI: | https://hdl.handle.net/1822/83758 |
Acesso: | Acesso aberto |
Aparece nas coleções: | BUM - Dissertações de Mestrado DET/2C2T - Dissertações de mestrado |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Ana Sofia da Silva Goncalves.pdf | 6,37 MB | Adobe PDF | Ver/Abrir |
Este trabalho está licenciado sob uma Licença Creative Commons