Utilize este identificador para referenciar este registo:
https://hdl.handle.net/1822/65318
Registo completo
Campo DC | Valor | Idioma |
---|---|---|
dc.contributor.advisor | Carneiro, O. S. | por |
dc.contributor.advisor | Viana, J. C. | por |
dc.contributor.advisor | Martins, Alexandrina | por |
dc.contributor.author | Ribeiro, Ana Sofia Costa | por |
dc.date.accessioned | 2020-05-11T10:21:08Z | - |
dc.date.available | 2020-05-12T06:00:12Z | - |
dc.date.issued | 2016 | - |
dc.date.submitted | 2016 | - |
dc.identifier.uri | https://hdl.handle.net/1822/65318 | - |
dc.description | Dissertação de mestrado integrado em Engenharia de Polímeros | por |
dc.description.abstract | A fratura de estofos de PVC é um problema de grande relevância que tem ganho cada vez mais atenção pelos fabricantes. No decorrer da dissertação, estudou-se a fractografia do ponto de vista mecânico, com o objetivo de determinar um parâmetro de fratura capaz de distinguir diferentes artigos de acordo com o seu comportamento no terreno. A aplicabilidade do trabalho essencial de fratura como parâmero de fratura foi avaliada para 4 artigos diferentes: três com base de PVC e um híbrido PVC/PU. Os artigos foram testados segundo três condições: à temperatura ambiente, após a extração de plastificante por contacto com óleos e a -10ºC. Os resultados obtidos foram comparados com métodos internos de teste aos materiais. Os resultados obtidos e as conclusões da dissertação são expostos no presente documento. | por |
dc.description.abstract | The fracture of PVC based upholstery is a problem of great relevance and has gained increasing attention by manufactures. During the development of the dissertation, the study was focused on fracture from a mechanical point of view, with the aim of finding a fracture parameter capable of discerning the different materials, in accordance with their behavior on the field. The applicability of the essential work of fracture as such parameter was assessed for four different materials: three with a PVC base and one hybrid PVC/PU. Materials were tested in three different conditions: room temperature, after plasticizer extraction by contact with oils, and at -10ºC. The results and conclusions drawn from the dissertation’s work are exposed in the present document. | por |
dc.language.iso | por | por |
dc.rights | openAccess | por |
dc.subject | Estofos de PVC | por |
dc.subject | Fractografia | por |
dc.subject | Trabalho essencial de fratura | por |
dc.subject | PVC upholstery | por |
dc.subject | Fractography | por |
dc.subject | Essential work of fracture | por |
dc.title | Análise da fratura em fissuras de estofos de PVC | por |
dc.type | masterThesis | eng |
dc.identifier.tid | 202473180 | por |
thesis.degree.grantor | Universidade do Minho | por |
sdum.degree.grade | 15 valores | por |
sdum.uoei | Escola de Engenharia | por |
dc.subject.fos | Engenharia e Tecnologia::Outras Engenharias e Tecnologias | por |
Aparece nas coleções: | BUM - Dissertações de Mestrado DEP - Dissertações de Mestrado |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Dissertação+66678+Ana+Sofia+Ribeiro.pdf | 2,68 MB | Adobe PDF | Ver/Abrir |