Título: | Comportamento ótico de diversos materiais após exposição a radiação UVC |
Outro(s) título(s): | Optical behavior of different materials after exposure to UVC radiation |
Autor(es): | Rodrigues, Ana Filipa Lopes Bago |
Orientador(es): | Franco, Sandra |
Palavras-chave: | Acrílicos Deformação Lâmpadas germicidas Radiação ultravioleta C Transmitância Acrylics Deformation Germicidal lamps Transmittance Ultraviolet C radiation |
Data: | 9-Fev-2022 |
Resumo(s): | Objetivo: Análise do comportamento ótico de alguns acrílicos aquando e após a exposição à radiação
ultravioleta C.
Métodos: A amostra foi constituída por 8 tipos de acrílicos, rígidos e flexíveis, tipicamente utilizados
no embalamento na indústria alimentar e protetores de balcões e objetos. Haviam 2 peças de cada
amostra sendo que uma foi exposta numa caixa escura e outra exposta numa caixa com lâmpadas
emissoras de UVC, lâmpadas TUV T8 Philips. As peças foram expostas por intervalos de tempo
idênticos nas respetivas caixas e entre cada exposição foi feita a medição de transmitância e da
deformação provocada por um peso previamente definido. Foram realizadas medições após uma
pausa na exposição ao UVC para verificar o quanto as peças alteravam as suas propriedades após a
exposição a esta radiação.
Resultados: Obtiveram-se dados de transmitância (%) para comprimentos de onda desde os 250 nm
até 1000 nm; de modo a verificar a similaridade entre os resultados obtidos em cada medição foi
calculado o índice de similaridade. Foram obtidos resultados da deformação provocada pelos pesos
determinados previamente. Foi ainda obtido o valor do índice de branqueamento e amarelecimento das
amostras;
Conclusões: Este estudo mostrou que a exposição às lâmpadas emissoras de UVC provocam
alterações na estrutura de alguns materiais, nomeadamente um caraterizado como protetor de
radiação ultravioleta, afetando propriedades óticas e físicas como transmitância e resistência dos
materiais. Verificou-se ainda que após uma pausa na exposição ao UVC determinadas peças
continuaram a sofrer alterações na sua estrutura. Objective: Analysis of the optical behavior of some acrylics when and after exposure to ultraviolet C radiation. Methods: The sample consisted of 8 types of acrylics, rigid and flexible, typically used in packaging in the food industry and protectors for counters and objects. There were 2 pieces of each sample, one was exposed in a dark box and the other exposed in a box with UVC emitting lamps, TUV T8 Philips lamps. The pieces were exposed for identical time intervals in the respective boxes and between each exposure the measurement of transmittance and deformation caused by a previously defined weight was taken. Measurements were taken after a break in UVC exposure to verify how much the pieces changed their properties after exposure to this radiation. Results: Transmittance data (%) were obtained for wavelengths from 250nm to 1000nm; in order to verify the similarity between the results obtained in each measurement, the similarity index was calculated. Results of the deformation caused by the previously determined weights were obtained. The whitening and yellowing index value of the samples was also obtained; Conclusions: this study showed that exposure to UVC emitting lamps causes changes in the structure of some materials, namely one characterized as a protector against ultraviolet radiation, affecting optical and physical properties such as transmittance and resistance of the materials. It was also found that after a break in exposure to UVC, certain pieces continued to undergo changes in their structure. |
Tipo: | Dissertação de mestrado |
Descrição: | Dissertação de mestrado em Optometria Avançada |
URI: | https://hdl.handle.net/1822/82026 |
Acesso: | Acesso aberto |
Aparece nas coleções: | BUM - Dissertações de Mestrado CDF - Dissertações de Mestrado / MSc Dissertations |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Ana Filipa Lopes Bago Rodrigues.pdf | 6,33 MB | Adobe PDF | Ver/Abrir |
Este trabalho está licenciado sob uma Licença Creative Commons